Product Name |
Mechanical properties of deposited metals |
Features and BXplications: |
TIG |
MIG |
Tensile strength Mpa |
Elongation (%) |
BX:307 |
612 |
43 |
Welding seam strength can be controlled. Primarily used for welding of austenitic manganese steel forgings and castings, and austenitic carbon steel forgings and castings with outstanding crack resistance. |
BX:308 |
607 |
41 |
Mainly used for welding of18Cr-8Ni steels with good-looking welding seam, outstanding crack resistance and stable electric arc. |
BX:308L |
578 |
42 |
Mainly used for welding of 18Cr-8Ni steels. The welding wires will have more outstanding corrosion resistance than MIG308, if they are used for welding of SUS304L. |
BX:309 |
607 |
40 |
Mainly used for welding of22Cr-12Ni steels, mild steels, chrome molybdenum steels. The welding wires can also be used for welding of SUS309S, SCS17 with outstanding heat resistance, good corrosion resistance, stable electric arc and excellent welding performance. |
BX:309L |
588 |
43 |
Mainly used for welding of low carbon stainless steels, low carbon Clad steels, SUS309S, 13Cr and 18Cr heat resisting steels, and heterogeneous metals with outstanding heat resistance and good corrosion resistance. |
BX:309Si |
557 |
32 |
Mainly used for welding of high silicon, low carbon, 22Cr-12Ni steels. |
BX:310 |
607 |
41 |
Mainly used for welding of25Cr-20Ni steels. Compared with MIG309, MIG309L, the welding wires are more suitable for welding of heavy metals, highly self hardened alloy steels and high carbon steels, and other profiles. |
BX:316 |
578 |
38 |
Mainly used for welding of18Cr-12Ni-2.5Mo(SUS316) steels with stable electric arc and good-looking welding bead. |
BX:316L |
558 |
41 |
Mainly used for welding of low-carbon-18Cr-12Ni-2.5Mo steels. Compared with MIG316, the welding wires have more outstanding corrosion resistance for welding of SUS316L. |
BX:316LSi |
562 |
31 |
Mainly used for welding ofhigh silicon, low carbon, -18Cr-12Ni-2.5Mo steels. |
BX:317 |
598 |
42 |
Mainly used for welding of18Cr-12Ni-3.5Mo steels. With outstanding resistance to sulphuric acid, sulphurous acid and other organic acids, exceptional resistance to pitting corrosion and heat, the welding wires are especially suitable for welding of chemical containers. |
BX:317L |
568 |
42 |
Mainly used for welding of low carbon 18Cr-12Ni-3.5Mo steels, low carbon and high molybdenum steels. The welding wires can avoid intergranular corrosion. Finished welded parts can free heat treatment. The welding wires have high-temperature strength and outstanding resistance to sulphuric acid, sulphurous acid and other organic acids. |
BX:321 |
562 |
39 |
Primarily used for welding of20Cr-10Ni-Ti steels. Thanks to Ti added, the welding wires have greatly increased resistance to intercrystalline corrosion. |
BX:347 |
627 |
41 |
Mainly used for welding of 18Cr-9Ni-Ti steels. Thanks to Nb added, the welding wires have greatly increased resistance to intergranular corrosion and outstanding high-temperature strength, especially suitable for welding of high temperature resisting steels. |
BX:410 |
510 |
25 |
Mainly used for welding of 13Cr steels. Deposited metals are 13Cr with large hardenability. Thanks to outstanding resistance to oxidation and corrosion at high temperature, the welding wires are especially suitable for welding of AISI410 or 420. |
4BX:430 |
585 |
36 |
Mainly used for welding of 17Cr steels, especially suitable for welding of nitric acid containers. |